CCI-Modified Bitumen Membrane is a Torch-applied bituminous felt reinforced with non-woven polyester mat and modified with APP elastomeric bitumen.
CCI-Modified Bitumen Membrane has cold flexibility property of -10°C.Produced in thickness of 4 mm CCI-Modified Bitumen Membrane is commercialized bottom and upper surfaces
protected by thermo-fusible PE film.
CCI-Modified Bitumen Membrane is a heavy duty felt reinforced with 250 gr/m2 non-woven polyester mat and used in civil engineering works; viaducts, bridges and tunnels on highways and railways.
Can be applied for upper layer of multi-layer build-up system or single layer.
Test Report:
Serial Number |
Items | Standard Specification |
Result | Remarks | |||||||||
1 | Mass per unit area, kg/m2 | 4.3 or higher | 4.5, 4.6, 4.4, 4.5, 4.5 | Passed | |||||||||
2 | Area, m2/roll | 10±0.10 | 10.01, 10.02, 10.01, 10.00, 10.01 |
Passed | |||||||||
3 | Thickness, mm | Average value | ≥4.0 | 4.1, 4.2, 4.0, 4.2, 4 | Passed | ||||||||
Minimum Value | 3.7 | 4.0,4.0,4.01,4.02,4.01 | Passed | ||||||||||
4 | Appearance | End face inside out, mm | Not exceed 10 | 3,5,6,3,7 | Passed | ||||||||
Feeling condition | The tire base should be soaked and there should be no unimpregnated areas. The surface should be flat, no holes, missing edges and cracks, bumps are allowed |
The tire base is soaked, surface is smooth, without holes, missing edges, cracks or bumps |
Passed | ||||||||||
Open book | When the coil is rolled out at any | No cracks | Passed |
product temperature (4- 60°C), there should be no cracks or adhesion of more than 10mm beyond the length of 1000mm from the core |
|||||||||||||
Joints | There should be no more than one, and the length of the shorter section should not be less than 1000mm. The joints should be cut neatly and lengthened by 150mm. |
No splices | Passed | ||||||||||
5 | Soluble content | ≥2900 | 3156 | Passed | |||||||||
6 | Heat resistance | 110°C Slide, mm | Upper Surface | ≤2 | 0 | Passed | |||||||
Lower Surface | 0 | Passed | |||||||||||
Test phenomena | No flowing or dripping | No flowing or dripping | Passed | ||||||||||
7 | Low temperature flexibility | -15°C, no cracks | No cracks | Passed | |||||||||
8 | Impermeable, 30 min | 0.3 MPa | 0.3 MPa, 30 mins waterproof | Passed | |||||||||
9 | Pull | Maximum peak,N/50mm | Longitudinal | ≥800 | 865 | Passed | |||||||
Landscape | 845 | Passed | |||||||||||
Test phenomena | During the tensile process, there is no cracking or separation of the asphalt coating layer from the tire base in the middle part of the specimen |
There is no cracking or separation of the asphalt coating layer from the tire base in the middle part of the specimen | Passed | ||||||||||
10 | Elongation | Maximum peak elongation, % |
Longitudinal | ≥40 | 48 | Passed | |||||||
Landscape | 46 | Passed | |||||||||||
11 | Mass increase after soaking, % | ≤1.0 | 0.6 | Passed | |||||||||
12 | Hot | Pull hold rate, % |
Longitudinal | ≥90 | 97 | Passed | |||||||
Landscape | 95 | Passed | |||||||||||
Elongation retention rate, % |
Longitudinal | ≥80 | 87 | Passed | |||||||||
Landscape | 86 | Passed | |||||||||||
Low temperature flexibility | -10°C, no cracks | No cracks | Passed | ||||||||||
Size change rate, % | ≤0.7 | 0.6 | Passed | ||||||||||
Quality loss, % | ≤1.0 | 0.7 | Passed | ||||||||||
13 | Seam peel strength, N/mm | ≥1.0 | 1.1 | Passed | |||||||||
14 | Thickness of asphalt coating on the bottom surface of the coil, mm | ≥1.0 | 1.2 | Passed | |||||||||
15 | Artificial climate acceleration | Appearance | No sliding, flowing, dripping | No sliding, flowing, dripping | Passed | ||||||||
Pull to keep aging rate, % | Longitudinal | ≥80 | 86 | Passed | |||||||||
Landscape | 85 | Passed | |||||||||||
Low temperature flexibility | -10°C, no cracks | No cracks | Passed |
General Application Steps:
Note:
-Rain, frost, snow and high humidity can interfere with the adhesion of the membrane. With temperatures below +2°C it is better to avoid the application.
-Before application the substrate must be clean and dry. Standing water should be removed from the deck surface before recommencing laying operations. Special care is required during installation to avoid damage to waterproofing membranes.
-If it is impossible to restrict access to the waterproofing professionals alone, temporary protection must be employed to protect the membrane from the level of traffic.
Packaging:
Note: 20Kgs of primer for 40sqm
Tools:
Roofing torch, propane cylinder, connecting hoses with regulator, trowel, knife and gloves.
Storage:
Protect material from heat and direct sunlight. Keep rolls in a vertical position and do not stack them.